JM3 Letters

Nanoimprint lithography of deoxyribonucleic acid biopolymer films

[+] Author Affiliations
Emily M. Fehrman Cory, Andrew Sarangan

University of Dayton, Electro-Optics Department, Dayton, Ohio 45469

Roberto S. Aga, Jr., Jack P. Lombardi, III, Carrie M. Bartsch, Emily M. Heckman

Sensors Directorate, Air Force Research Laboratory, Wright-Patterson AFB, Ohio 45433

J. Micro/Nanolith. MEMS MOEMS. 12(4), 040501 (Dec 16, 2013). doi:10.1117/1.JMM.12.4.040501
History: Received April 10, 2013; Revised October 10, 2013; Accepted October 24, 2013
Text Size: A A A

Open Access Open Access

Abstract

Abstract.  Thermal nanoimprint lithography (NIL) is presented as an alternative fabrication technique for patterning deoxyribonucleic acid (DNA) biopolymer films for photonic device applications. The techniques and procedures developed for directly imprinting optical waveguide structures on a DNA biopolymer using NIL, bypassing the use of a resist layer and any chemical processing, are outlined here. The fabrication technique was developed with a Nanonex NX-2600 NIL flexible membrane system. Additionally, a process for using a Suss MicroTec ELAN CB6L substrate bonder is discussed as an alternative to commercially available NIL systems.

Figures in this Article

The marine-derived deoxyribonucleic acid (DNA) biopolymer has been demonstrated in a wide range of photonic devices, including organic light emitting diodes, organic field effect transistors, and polymer electro-optic (EO) modulators.14 The DNA biopolymer is an especially promising material as a cladding layer for poled polymer EO-waveguide devices. Compared to the standard cladding material UV15 commonly used in these devices, the DNA biopolymer cladding layer yields polymer waveguide devices with EO coefficients 2× greater, optical losses more than an order of magnitude lower, and increased solvent compatibility with common polymer core materials.5,6 However, patterned EO modulators have yet to be fabricated that take advantage of these enhanced material properties due to the incompatibility of the DNA biopolymer with photolithography and chemical processing techniques. As an alternative to photolithography, thermal nanoimprint lithography (NIL) has been identified as a technique for pattering the DNA biopolymer. The NIL is a nonoptical pattern transfer method originally developed as a cost-effective alternative to electron beam lithography.710 This paper outlines the techniques and procedures developed for directly imprinting optical waveguide structures on the DNA biopolymer using NIL, allowing patterned EO modulators to be fabricated using the DNA biopolymer for enhanced performance.

An inverted ridge waveguide designed for 1550 nm is patterned in the DNA biopolymer as a passive bottom cladding layer for an EO waveguide device. Unlike conventional NIL where a thermal resist layer is imprinted as an etch mask,7,8 the waveguide pattern is directly imprinted into the biopolymer film thereby preventing damage to the material by removing exposure to resists, etchants, and solvents. The 3 in. stamps are designed to imprint channels that are 0.2-μmdeep×4-μmwide into a 2-μm thick DNA biopolymer film, with length extending over a full 3 in. wafer. After imprinting, the residual layer is retained as the bottom cladding of the inverted ridge waveguide (Fig. 1). Imprinting a depressed channel in the cladding layer as opposed to a raised ridge in the core layer displaces a smaller amount of material and improves the quality of pattern transfer.11

Graphic Jump LocationF1 :

(a) Schematic of the nanoimprint lithography (NIL) process showing the deoxyribonucleic acid (DNA) biopolymer film pre- and postimprint (b) the electro-optic (EO) modulator waveguide device structure with a DNA biopolymer cladding on either side of the EO active core polymer.

The DNA used in this study was derived from salmon and precipitated with a surfactant, hexadecyltrimethyl-ammonium chloride (CTMA), to form the water-insoluble biopolymer, DNA-CTMA. Details of the DNA-CTMA processing technique can be found in prior publications.12 The DNA biopolymer is dissolved at 14 wt% in butanol, spin coated on gold-coated Si substrates, and cured in vacuum at 80°C to produce 2-μm-thick films. The evaporated gold film on the Si substrate serves the dual purpose of an adhesion coating and a bottom electrode for the EO modulator. The edge bead on the DNA-CTMA, an artifact from spin coating, was removed with a razor blade to provide a level surface for NIL.

NIL stamps have been developed using various materials, including silicon, glass, SU-8, and polymers.714 Electron-beam writing is often used for stamps with submicron scale features and photolithography is used for larger-scale features. For this study, the minimum feature sizes were large enough that photolithography was used to fabricate the stamp. Three stamp materials (plasma etched Si, plasma etched SiO2 on a Si substrate, and the negative UV curable resist MicroChem SU-8 2015 on a Si substrate) were initially compared for compatibility with the DNA biopolymer. However, because SU-8 2015 was found to aggressively stick to the DNA biopolymer, it was not pursued as a stamp material. All stamps were 3 in. wafers, and were used in conjunction with film samples on 3 in. substrates.

Three release coatings were investigated for use on the Si and SiO2 stamps: perfluorodecyltrichlorosilane (FDTS), chlorinated organopolysiloxane Sigma-Aldrich (St. Louis, Missouri) Sigmacote, and the chlorosilane Nanonex (Monmouth Jct., New Jersey) NXT-130 mold release agent. For the FDTS coating, 1 g of FDTS was diluted in 75 mL of n-heptane, the stamp was submerged for 4 min, rinsed in a bath of n-heptane for 20 s, rinsed in a fresh bath of n-heptane for 5 min, then dried on a hotplate at 130°C for 10 min. For Sigmacote, a pipette was used to fully cover the surface of the stamp, it was rinsed with deionized water after 2 s, then baked in a vacuum at 130°C for 1 h. The Nanonex NXT-130 was applied by vapor coating with the Nanonex Ultra-100 Molecular Vapor Coater for 25 min at 90°C. All of the release coatings performed equally well; however, due to the ease of application, Sigmacote is the preferred release coating.

The Nanonex NX-2600 NIL system was used in this work and its performance is compared with a Suss MicroTec (Garching, Germany) ELAN CB6L substrate bonder. Although the Suss bonder is not an NIL system, it performs similarly by applying high pressures and temperatures through parallel plates. The NIL process for both systems involves four steps: (1) the chamber pump-down (NIL performed under vacuum), (2) preimprint step (temperature raised to the glass transition temperature Tg of material to be imprinted and pressure gradually increased), (3) imprint step (imprint pressure and temperature applied for set time), and (4) the cool down/chamber vent (imprint pressure maintained until sample is cooled) (Fig. 2).7,8 The stamp and sample are then separated manually, assisted by wedging a thin blade between the wafers and blowing compressed air between the wafers. A temperature Tg of the polymer material is used as the NIL imprint step temperature. The Tg of the DNA biopolymer was measured to be 90 to 110°C for a 1-μm-thick film by shear force modulation spectroscopy. The DNA biopolymer is thermally stable to 200°C.15 An imprint temperature, 120°C and 200°C, was necessary for 11 pattern transfer. Since DNA-CTMA is a highly viscous polymer, the maximum pressure setting of 500 psi for the Nanonex tool was used. Pressures less than 500 psi resulted in partial pattern transfer from the stamp to the polymer film characterized by soft edges and reduced feature depth. The imprint step time was 3 to 5 min to allow the DNA biopolymer adequate time to flow into all parts of the stamp, creating a 11 pattern transfer.

Graphic Jump LocationF2 :

Pressure and temperature cycles for the NIL process for the DNA biopolymer using the Nanonex NX-2600. The four imprint stages are: (1) pump-down where the chamber is placed under vacuum, (2) preimprint where the temperature raised to the glass transition temperature, Tg, of the material and the pressure is gradually increased, (3) imprint where the imprint pressure and temperature are applied for a set time, and (4) cool down/chamber vent where the imprint pressure is maintained until the sample is cooled.

A summary of the NIL results are shown in Table 1. Although NIL patterned surfaces are often characterized by cross-sectional scanning electron microscope (SEM) images, profile scans, and atomic force microscope (AFM) surface scans,16,17 this was not possible with the DNA biopolymer since the film tends to tear at the cleaved edge and obscures the cross-sectional view. Therefore, a qualitative classification method of “excellent,” “good,” or “poor” was used to describe the imprinted NIL pattern. Excellent indicates a 11 pattern transfer with straight sidewalls, minimal roughness, and fully developed corners; this was achieved with the Nanonex system using a NIL recipe of 120°C at 500 psi for 3 min with a release coated SiO2 stamp. Scattering loss for surface roughness <100nm is expected to be negligible due to the 1550-nm operating wavelength. Additionally, slightly rounded corners are expected due to the viscous nature of the biopolymer which is unable to fully conform to the sharp stamp features. For excellent pattern transfer, the pattern appears to be complete and uniform along the full length of the waveguides (2 to 3 in.). Good indicates correct imprint depth but with overly rounded corners and rough sidewalls due to incomplete filling of the stamp pattern. Poor indicates that the biopolymer film adhered to the sidewalls or other features of the stamp resulting in tearing of the film. This qualitative pattern transfer classification is demonstrated by the SEM, micrograph, and AFM images (Fig. 3). As shown in Fig. 3(d), some pitting defects occur in the spaces between the waveguide features, another indication of incomplete filling of the stamp.

Table Grahic Jump Location
Table 1Summary of nanoimprint lithography (NIL) recipe performance comparing Nanonex flexible membrane system and Suss rigid plate system. The imprint quality descriptors “excellent,” “good,” and “poor” are defined in the text.

Graphic Jump LocationF3 :

The NIL-patterned waveguide channel in the DNA biopolymer with (a) “excellent” imprint quality (SEM image), (b) “good” imprint quality (SEM image), (c) “poor” imprint quality of 15-μm wide channel (micrograph), and (d) “good” imprint quality (AFM image). The imprint quality descriptors “excellent,” “good,” and “poor” are defined in the text.

Excellent pattern transfer was also achieved with the Suss MicroTec substrate bonder. However, to achieve uniform pattern transfer, it was necessary to sandwich the stamp and polymer film wafers between two 0.020-in.-thick sheets of Teflon polytetrafluoroethylene (PTFE) (McMaster-Carr, Aurora, Ohio) inside the parallel plates to compensate for nonplanarities of the rigid plates and mimic the pressure-equalizing effect of the flexible membranes of the Nanonex system. An NIL recipe of 150°C at 500 psi for 5 min using the Suss bonder with PTFE sheets resulted in excellent pattern transfer, of the same quality achieved on the Nanonex system.

In summary, an NIL process was developed and characterized for directly imprinting photonic waveguide structures in a DNA biopolymer using both a commercial NIL system and an in-house adapted NIL system using a Suss substrate bonder. Identifying NIL as a patterning method for DNA biopolymer photonic structures allows for fabricating a wide variety of photonic and electronic devices that are unattainable using conventional wet photolithographic techniques. It has been shown that micron-scale features that are traditionally achievable only by photolithography can be successfully transferred to the DNA biopolymer through NIL. Future work using stamps fabricated by e-beam lithography has the potential to push the feature sizes to the nano-scale for DNA biopolymer devices.

References

Grote  J. et al., “DNA: new class of polymer,” Proc. SPIE. 6117, , 61170J  (2006). 0277-786X CrossRef
Hagen  J. et al., “Enhanced emission efficiency in organic light-emitting diodes using deoxyribonucleic acid complex as an electron blocking layer,” Appl. Phys. Lett.. 88, (17 ), 171109  (2006). 0003-6951 CrossRef
Singh  B. et al., “Bio-organic-semiconductor-field-effect-transistor based on deoxyribonucleic acid gate dielectric,” J. Appl. Phys.. 100, (2 ), 024514  (2006). 0021-8979 CrossRef
Heckman  E. M. et al., “DNA biopolymer conductive cladding for polymer electro-optic waveguide modulators.” Appl. Phys. Lett.. 98, (10 ), 103304  (2011). 0003-6951 CrossRef
Heckman  E. et al., “Advances in DNA photonics,” Proc. SPIE. 8464, , 84640P  (2012). 0277-786X CrossRef
Aga  R. et al., “Polymeric waveguide electro-optic beam-steering device with DNA biopolymer conductive cladding layers,” Opt. Eng.. 51, (11 ), 114602  (2012). 0091-3286 CrossRef
Chou  S. Y., Krauss  P. R., Renstrom  P. J., “Nanoimprint lithography,” J. Vac. Sci. Technol. B.. 14, (6 ), 4129 –4133 (1996). 0734-211X CrossRef
Guo  L. J., “Nanoimprint lithography: methods and material requirements,” Adv. Mat.. 19, (4 ), 495 –519 (2007). 0935-9648 CrossRef
Schift  H., “Nanoimprint lithography: an old story in modern times? a review,” J. Vac. Sci. Technol. B.. 26, (2 ), 458 –480 (2008). 0734-211X CrossRef
Zankovych  S. et al., “Nanoimprint lithography: challenges and prospects,” Nanotechnology. 12, (2 ), 91 –95 (2001). 0957-4484 CrossRef
Gourgon  C. et al., “Influence of pattern density in nanoimprint lithography,” J. Vac. Sci. Technol. B.. 21, (1 ), 98 –105 (2003). 0734-211X CrossRef
Ouchen  F. et al., “Modified processing techniques of a DNA biopolymer for enhanced performance in photonics applications,” Appl. Phys. Lett.. 101, (15 ), 153702  (2012). 0003-6951 CrossRef
Ding  Y. et al., “Relaxation behavior of polymer structures fabricated by nanoimprint lithography,” ACS Nano.. 1, (2 ), 84 –92 (2007). 1936-0851 CrossRef
Hirai  Y., Yoshida  S., Takagi  N., “Defect analysis in thermal nanoimprint lithography,” J. Vac. Sci. Technol. B.. 21, (6 ), 2765 –2770 (2003). 0734-211X CrossRef
Heckman  E. et al., “DNA biopolymer conductive cladding for polymer electro-optic waveguide modulators,” Appl. Phys. Lett.. 98, , 103304  (2011). 0003-6951 CrossRef
Chaix  N. et al., “Influence of the molecular weight and imprint conditions on the formation of capillary bridges in nanoimprint lithography,” Nanotechnology. 17, (16 ), 4082 –4087 (2006). 0957-4484 CrossRef
Erenturk  B. et al., “Fabrication of air gap dielectrics by nanoimprint lithography,” Microelectron. Eng.. 98, , 89 –96 (2012). 0277-786X CrossRef

© The Authors. Published by SPIE under a Creative Commons Attribution 3.0 Unported License. Distribution or reproduction of this work in whole or in part requires full attribution of the original publication, including its DOI.

Citation

Emily M. Fehrman Cory ; Roberto S. Aga, Jr. ; Jack P. Lombardi, III ; Carrie M. Bartsch ; Andrew Sarangan, et al.
"Nanoimprint lithography of deoxyribonucleic acid biopolymer films", J. Micro/Nanolith. MEMS MOEMS. 12(4), 040501 (Dec 16, 2013). ; http://dx.doi.org/10.1117/1.JMM.12.4.040501


Figures

Graphic Jump LocationF1 :

(a) Schematic of the nanoimprint lithography (NIL) process showing the deoxyribonucleic acid (DNA) biopolymer film pre- and postimprint (b) the electro-optic (EO) modulator waveguide device structure with a DNA biopolymer cladding on either side of the EO active core polymer.

Graphic Jump LocationF2 :

Pressure and temperature cycles for the NIL process for the DNA biopolymer using the Nanonex NX-2600. The four imprint stages are: (1) pump-down where the chamber is placed under vacuum, (2) preimprint where the temperature raised to the glass transition temperature, Tg, of the material and the pressure is gradually increased, (3) imprint where the imprint pressure and temperature are applied for a set time, and (4) cool down/chamber vent where the imprint pressure is maintained until the sample is cooled.

Graphic Jump LocationF3 :

The NIL-patterned waveguide channel in the DNA biopolymer with (a) “excellent” imprint quality (SEM image), (b) “good” imprint quality (SEM image), (c) “poor” imprint quality of 15-μm wide channel (micrograph), and (d) “good” imprint quality (AFM image). The imprint quality descriptors “excellent,” “good,” and “poor” are defined in the text.

Tables

Table Grahic Jump Location
Table 1Summary of nanoimprint lithography (NIL) recipe performance comparing Nanonex flexible membrane system and Suss rigid plate system. The imprint quality descriptors “excellent,” “good,” and “poor” are defined in the text.

References

Grote  J. et al., “DNA: new class of polymer,” Proc. SPIE. 6117, , 61170J  (2006). 0277-786X CrossRef
Hagen  J. et al., “Enhanced emission efficiency in organic light-emitting diodes using deoxyribonucleic acid complex as an electron blocking layer,” Appl. Phys. Lett.. 88, (17 ), 171109  (2006). 0003-6951 CrossRef
Singh  B. et al., “Bio-organic-semiconductor-field-effect-transistor based on deoxyribonucleic acid gate dielectric,” J. Appl. Phys.. 100, (2 ), 024514  (2006). 0021-8979 CrossRef
Heckman  E. M. et al., “DNA biopolymer conductive cladding for polymer electro-optic waveguide modulators.” Appl. Phys. Lett.. 98, (10 ), 103304  (2011). 0003-6951 CrossRef
Heckman  E. et al., “Advances in DNA photonics,” Proc. SPIE. 8464, , 84640P  (2012). 0277-786X CrossRef
Aga  R. et al., “Polymeric waveguide electro-optic beam-steering device with DNA biopolymer conductive cladding layers,” Opt. Eng.. 51, (11 ), 114602  (2012). 0091-3286 CrossRef
Chou  S. Y., Krauss  P. R., Renstrom  P. J., “Nanoimprint lithography,” J. Vac. Sci. Technol. B.. 14, (6 ), 4129 –4133 (1996). 0734-211X CrossRef
Guo  L. J., “Nanoimprint lithography: methods and material requirements,” Adv. Mat.. 19, (4 ), 495 –519 (2007). 0935-9648 CrossRef
Schift  H., “Nanoimprint lithography: an old story in modern times? a review,” J. Vac. Sci. Technol. B.. 26, (2 ), 458 –480 (2008). 0734-211X CrossRef
Zankovych  S. et al., “Nanoimprint lithography: challenges and prospects,” Nanotechnology. 12, (2 ), 91 –95 (2001). 0957-4484 CrossRef
Gourgon  C. et al., “Influence of pattern density in nanoimprint lithography,” J. Vac. Sci. Technol. B.. 21, (1 ), 98 –105 (2003). 0734-211X CrossRef
Ouchen  F. et al., “Modified processing techniques of a DNA biopolymer for enhanced performance in photonics applications,” Appl. Phys. Lett.. 101, (15 ), 153702  (2012). 0003-6951 CrossRef
Ding  Y. et al., “Relaxation behavior of polymer structures fabricated by nanoimprint lithography,” ACS Nano.. 1, (2 ), 84 –92 (2007). 1936-0851 CrossRef
Hirai  Y., Yoshida  S., Takagi  N., “Defect analysis in thermal nanoimprint lithography,” J. Vac. Sci. Technol. B.. 21, (6 ), 2765 –2770 (2003). 0734-211X CrossRef
Heckman  E. et al., “DNA biopolymer conductive cladding for polymer electro-optic waveguide modulators,” Appl. Phys. Lett.. 98, , 103304  (2011). 0003-6951 CrossRef
Chaix  N. et al., “Influence of the molecular weight and imprint conditions on the formation of capillary bridges in nanoimprint lithography,” Nanotechnology. 17, (16 ), 4082 –4087 (2006). 0957-4484 CrossRef
Erenturk  B. et al., “Fabrication of air gap dielectrics by nanoimprint lithography,” Microelectron. Eng.. 98, , 89 –96 (2012). 0277-786X CrossRef

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging & repositioning the boxes below.

Related Book Chapters

Topic Collections

Advertisement
  • Don't have an account?
  • Subscribe to the SPIE Digital Library
  • Create a FREE account to sign up for Digital Library content alerts and gain access to institutional subscriptions remotely.
Access This Article
Sign in or Create a personal account to Buy this article ($20 for members, $25 for non-members).
Access This Proceeding
Sign in or Create a personal account to Buy this article ($15 for members, $18 for non-members).
Access This Chapter

Access to SPIE eBooks is limited to subscribing institutions and is not available as part of a personal subscription. Print or electronic versions of individual SPIE books may be purchased via SPIE.org.