Comparison of picosecond laser sources for SiNx ablation with subsequent nickel silicide formation by excimer laser annealing (ELA) for high efficiency silicon solar cells

S. Gall; J. Vibert; M. Pirot; J.-F. Lerat; T. Emeraud; N. Le Quang; Abdelilah Slaoui; A. Bahouka

doi:10.1117/12.2025560

16 September 2013 Comparison of picosecond laser sources for SiNx ablation with subsequent nickel silicide formation by excimer laser annealing (ELA) for high efficiency silicon solar cells

S. Gall, J. Vibert, M. Pirot, J.-F. Lerat, T. Emeraud, N. Le Quang, Abdelilah Slaoui, A. Bahouka

Author Affiliations +

Proceedings Volume 8826, Laser Material Processing for Solar Energy Devices II; 882609 (2013) https://doi.org/10.1117/12.2025560
Event: SPIE Solar Energy + Technology, 2013, San Diego, California, United States

Abstract

We compare two types of laser ablation for ARC removal on polished and textured surfaces. Selective ablation with limited impact on the underlying substrate is performed with short wavelength picosecond sources working at relatively low repetition rate (<200 kHz). By adapting wavelength and fluence, the SiNx could be removed efficiently with slight change initial topography. Crystal damage is detected whatever the laser parameters but could be reduced using low fluence in UV regime. The second ablation process uses ultra-high repetition rate picosecond laser (80 MHz) and targets both SiNx ablation and over-doping of the initial n⁺ emitter. The thermal effect induced by the short duration between pulses performs simultaneously SiNx removal and selective emitter structure with with deep dopant profiles and low surface concentration. We investigate the correlation between the post-ablation properties and a nickel silicidation process using Excimer Laser Annealing of a thin layer of Ni. A reference process is first described on pyramid topography without pre-ablation of SiN_x. It is demonstrated efficient formation of SixNiy compounds on the silicon substrate depending and laser fluence. The similar silicidation process is transferred on sample after the SiN_x ablation step. A continuous nickel silicide layer is observed but its thickness distribution reveals non-uniformity over the pyramids due to post ablation roughness.

Citation Download Citation

S. Gall, J. Vibert, M. Pirot, J.-F. Lerat, T. Emeraud, N. Le Quang, Abdelilah Slaoui, and A. Bahouka "Comparison of picosecond laser sources for SiNx ablation with subsequent nickel silicide formation by excimer laser annealing (ELA) for high efficiency silicon solar cells", Proc. SPIE 8826, Laser Material Processing for Solar Energy Devices II, 882609 (16 September 2013); https://doi.org/10.1117/12.2025560

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE