23 November 2022 Direct laser writing breaking diffraction barrier based on two-focus parallel peripheral-photoinhibition lithography
Dazhao Zhu, Liang Xu, Chenliang Ding, Zhenyao Yang, Yiwei Qiu, Chun Cao, Hongyang He, Jiawei Chen, Mengbo Tang, Lanxin Zhan, Xiaoyi Zhang, Qiuyuan Sun, Chengpeng Ma, Zhen Wei, Wenjie Liu, Xiang Fu, Cuifang Kuang, Haifeng Li, Xu Liu
Author Affiliations +
Abstract

Direct laser writing (DLW) enables arbitrary three-dimensional nanofabrication. However, the diffraction limit poses a major obstacle for realizing nanometer-scale features. Furthermore, it is challenging to improve the fabrication efficiency using the currently prevalent single-focal-spot systems, which cannot perform high-throughput lithography. To overcome these challenges, a parallel peripheral-photoinhibition lithography system with a sub-40-nm two-dimensional feature size and a sub-20-nm suspended line width was developed in our study, based on two-photon polymerization DLW. The lithography efficiency of the developed system is twice that of conventional systems for both uniform and complex structures. The proposed system facilitates the realization of portable DLW with a higher resolution and throughput.

1.

Introduction

Peripheral photoinhibition (PPI) direct laser writing (DLW) is a lithography technology used to improve the feature size in two-photon polymerization (2PP) DLW.14 In the concept and implementation, it is analogous to stimulated-emission depletion microscopy,57 which uses two beams with opposite functions: a Gaussian-shaped induction beam causing fluorescence excitation and a doughnut-shaped inhibition beam quenching it at the periphery.8 Subdiffraction PPI-DLW relies on the precise spatiotemporal overlapping of these two beams.9 In the peripheral region, photoexcitation of the Gaussian-shaped beam is inhibited and polymerization is prevented; therefore, only the central excited region is polymerized.1013 In this way, nanofeature sizes breaking the diffraction barrier can be achieved.

Previous scholars have reported minimum lateral feature sizes below 100 nm.1,11,14 Cao et al.15 achieved a 40-nm feature size and a 130-nm resolution with excitation and inhibition beam wavelengths of 488 and 375 nm, respectively. Gan et al.8 achieved a single line with a 9-nm feature size and two adjacent lines with a 52-nm resolution using excitation and inhibition beam wavelengths of 800 and 375 nm, respectively. He et al.16 applied a twin-oval-shaped beam instead of a doughnut-shaped beam in PPI-DLW with excitation and inhibition beam wavelengths of 800 and 532 nm, respectively, and stably obtained a 45-nm single nanowire.

DLW is remarkably advantageous, due to its maskless and vacuum-free operation, three-dimensional (3D) lithography capability,17 and cost-effectiveness.1820 Therefore, it has been used to fabricate many functional nanostructures that are employed in photonics,2123 electronics,2427 and life sciences.2830 In addition to the aforementioned advantages, PPI-DLW offers a subdiffraction feature size, making it a powerful tool for the fields mentioned above.2830

However, the throughput of single-beam/spot DLW is a noticeable disadvantage that greatly restricts the applicability of PPI-DLW.31 This problem can be addressed by performing parallel lithography with multifocal arrays, especially when fabricating periodic structures.3235 Since 2005, several research groups have aimed at such multipoint parallel processing. Multispot generation methods include the use of microlens arrays, beam-splitting devices, spatial light modulators (SLMs), and deformable-mirror devices (DMDs). Microlens arrays and beam-splitting devices are less flexible than SLMs and DMDs.

Among these devices, SLMs3641 are the most commonly used. Wegener et al.42 implemented a system using diffraction elements to achieve nine points and printed a metamaterial structure containing 108,000 3D units. In PPI-DLW, both Gaussian- and doughnut-shaped multifocal beams can be generated via phase modulation with an SLM.33 Before printing, many phase maps are needed; they can be acquired via phase-retrieving arithmetic based on the pattern or structure to be printed. The phase maps uploaded on the SLM control the light field (specifically the beam on–off). As the beam is scanned, the phase map loaded on the SLM is continuously switched. Thus the individual and dynamic on–off control of a single spot in an array is restricted by the SLM frame rate. Moreover, if the pattern or structure is quite complex and nonperiodic, the iterative Fourier transform required for the phase map is time- and hard-drive-memory-consuming.43,44 Consequently, the overall efficiency of multifocal-based printing is restricted. Therefore, more efficient on–off control methods would be highly desirable to improve the printing speed of multifocal systems.

To overcome these challenges and restrictions, this paper reports a parallel peripheral-photoinhibition lithography (P3L) system that attains a subdiffraction feature size and improves the lithography efficiency, outperforming the currently prevalent single-focal-spot systems. To double the efficiency, the proposed P3L system employs two printing channels, each of which is formed by an excitation solid spot and an inhibition doughnut spot to realize PPI. The individual control of each channel enables them to print different patterns simultaneously, resulting in a system that is more functional than one with a uniform focus control. The position and separation of the spots can also be easily controlled, making the system flexible. The proposed P3L system can achieve a sub-40-nm two-dimensional (2D) feature size and a sub-20-nm suspended line width. The remainder of this paper is organized as follows. Section 2 describes the proposed system, with further details in the Supplementary Material. In Sec. 3, many experiment results including feature size verification and 3D structure parallel printing are presented. A discussion and outlook are provided in Sec. 4. Finally, this work is concluded in Sec. 5.

2.

Materials and Methods

2.1.

Proposed System

For the excitation and inhibition beams, the polarization property of light is used to generate two focal spots by utilizing an SLM, corresponding to the s- and p-polarized components of the beam. Individual and dynamic on–off and aberration control can be realized for both the excitation and inhibition spots. Figure 1(a) provides a schematic of the proposed system, and Fig. 1(b) depicts its physical arrangement. The system includes eight modules numbered 1–8, as shown in Fig. 1(b). First, the s- and p-polarized components of the beam are split so that they can be individually controlled; then they are modulated by the left and right tilt phase masks (loaded on the SLM) so that the s- and p-components generate two separate spots after focusing. The distances between the spots and their positions can be adjusted using the tilt coefficient. For the inhibition beam, a vortex phase (loaded on the SLM) is utilized to generate a doughnut spot. The wavelength of the excitation beam is 780 nm (Coherent, Chameleon Vision II, 3 W, Glasgow, UK; pulsed 80-MHz repetition rate), and that of the inhibition beam is 532 nm (Laser Quantum, Opus 532-5W, Stockport, UK; continuous wave). Modules 1 and 2, 3 and 4, and 5 and 6 are the same; they differ only in having different optical elements fit for different wavelengths. Modules 1 and 2 (MRC, Heidelberg, Germany) are used for beam-pointing stabilization. Modules 3 and 4 first split the excitation/inhibition beam into two beams using a polarizing beam splitter (PBS), so that the individual on–off control of each beam can be realized using an acoustic-optical modulator (AOM). Then the two beams are recombined using another PBS. Modules 5 and 6 perform phase modulation using SLMs. The polarization property of SLMs is completely leveraged; the s- and p-components are modulated by different areas on the SLM screen, and a quarter-wave plate is used for the polarization shift.45,46 In module 7, the excitation and inhibition beams are combined and then successively passed through a galvanometer scanner (CTI, 8310K, Lexington, Massachusetts) and a scan lens (Nikon, PROJ-XSD007835 A1, Tokyo, Japan). In module 8, a microscope with an objective lens (Nikon, NA 1.45, 100×, Tokyo, Japan) is used for beam focusing and photoresist-sample holding. Additional details regarding each module and the entire system are provided in Figs. S1–S5 in the Supplementary Material.

Fig. 1

Proposed P3L system and focal spots: (a) schematic of the P3L system and (b) physical arrangement with eight modules. (c), (d) Focal spots located near the xy and yz planes, respectively. The light blue and green spots were generated by the 532-nm beam, and the purple and red spots were produced by the 780-nm beam, forming two combinations. The combination of light blue and purple spots was named channel 1, and the other combination was named channel 2. (c) and (d) share the same scale bar.

AP_4_6_066002_f001.png

The scanning imaging function was utilized to verify the quality of the spots (two excitation solid spots and two inhibition doughnut spots) by imaging 150-nm-diameter gold beads, as shown in Figs. 1(c) and 1(d), in which one excitation solid spot and one inhibition doughnut spot are superposed in three dimensions. The 02π vortex phase was used to modulate the inhibition light. The primary wavefront aberrations were corrected carefully by applying Zernike polynomials.47,48 To present the features of our system concisely, a pattern containing two lines of the test is shown in Fig. S6 in the Supplementary Material. The final phase masks loaded on the SLMs are depicted in Figs. S7(a) and S7(b) in the Supplementary Material. The distances and relative positions of the two spots were quantitatively controlled by adjusting the tip and tilt coefficient through careful calibration. The system was also used to generate a traditional 3D dark spot (Fig. S8 in the Supplementary Material).

2.2.

PSF Verification and Image Acquisition

The galvanometer, AOM, piezostage, and trigger signals to the PMT were controlled by external voltages. An eight-channel analog-out card (National Instruments, NI PXIe-6733, Austin, Texas) provided these voltage signals, and another DAQ card (National Instruments, NI PXIe-6363, Austin, Texas) was used for data acquisition. The two cards were synchronized via a PXIe chassis (National Instruments, NI PXIe-1073, Austin, Texas), which was controlled through a manufacturer-supplied dynamic link library and C++ software developed in-house. Scanning could be conducted in any region of interest in the xy, xz, and yz planes, and images could be automatically acquired once the parameters were set.

2.3.

Printing Manner and Monitoring

Except for the cubic metamaterial sample, which was printed in a dip-in manner, all the samples in this study were printed in the conventional oil–substrate–photoresist manner: the objective lens on the inverted microscope was immersed in oil and the photoresist was presented on the substrate. We used a glass slide as a substrate (refractive index: 1.51) and fixed it on the piezostage using a specially designed adaptor holder. The widefield image was acquired by a charge-coupled device camera, and the software was provided by the manufacturer. Four instant snapshots taken during the parallel printing process for the two lines of text are shown in Fig. S7(c) in the Supplementary Material (Video 1, MP4, 6.995 MB [URL: https://doi.org/10.1117/1.AP.4.6.066002.s1]). The substrate was illuminated from above by a light-emitting diode light source (wavelength, 625 nm, Thorlabs, CHROLITS-C1, Newton, New Jersey; driver, Thorlabs, LEDD1B, Newton, New Jersey). All the laser powers were measured at the aperture before the objective lens on the microscope by a power meter (power sensor, S121C, Thorlabs; power and energy meter console, Thorlabs, Newton, New Jersey).

2.4.

Materials and Sample Processing

A formulation containing 0.5 g of 7-diethylamino-3-thenoylcoumarin, 8.6 g of tricyclodecane dimethanol diacrylate, 0.7 g of ethoxylated bisphenyl fluorene diacrylate, and 0.7 g of o-phenyl phenoxyethyl acrylate was used as the sample photoresist.49 The exposed samples were developed in propylene glycol 1-monomethyl ether 2-acetate for 15 min, followed by rinsing in isopropanol for 5 min. A 2-nm-thick gold layer was evaporated on the samples prior to topography observation.

3.

Results

3.1.

2D Sub-40-nm Feature Size Verification

We printed a nanowire on a glass substrate (170-μm-thick microscope coverslip) with and without PPI to verify the feature size of our system. Many previous works have shown that, for a certain focal-spot speed, the final feature size is sensitive to both the excitation and inhibition powers. The spot speed was set to 1  mm/s, and five excitation powers were chosen for each inhibition power, as shown in Fig. 2(a). Figure 2(b) shows a scanning electron microscopy (SEM) image of the nanowire at the excitation and inhibition powers indicated by the red box in Fig. 2(a), demonstrating that the line width is reduced from 138.8 to 39.8 nm. Suspended nanowires were also printed for further demonstration, and the experimental results are presented in Figs. S9 and S10 in the Supplementary Material.

Fig. 2

Two-dimensional feature size verification experiment results. (a) Feature size versus inhibition beam intensity under excitation beam exposure with different powers. (b) SEM image of the nanowire obtained at the point in the red box in (a). After the PPI is turned on, the line width is compressed from 138.8 to 39.8 nm. Scale bar: 100 nm.

AP_4_6_066002_f002.png

3.2.

Bit Dot Pattern Printing

Because large data-recording systems are important potential applications of multifocal DLW,33 we printed a bit pattern to verify the feasibility of our system. The pattern in Fig. S6 in the Supplementary Material was pixelated and reprinted using PPI-2PP and 2PP. The pitch of the bits was set to 200 nm. The dwell time of one dot was 8  μs, the excitation spot power was 14.5 mW, and the inhibition power was 41.0 mW. The results are presented in Fig. 3: the bit dots printed with PPI [upper line in Fig. 3(a)] are clearly resolved with distinct gaps; by contrast, the bit dots printed without PPI [lower line in Fig. 3(a)] are blurred. The two lines of text were still printed simultaneously, whereas the two lines must be printed individually in a normal single-beam-path system. Consequently, the efficiency of our method is twice that of a normal single-beam-path system. Further experimental verification can be found in Fig. S11(a) in the Supplementary Material, which depicts two different bit dot patterns printed by two channels with PPI. In addition, two square-wave patterns with a 150-nm bit gap were printed, and the results are presented in Figs. S11(b) and S11(c) in the Supplementary Material.

Fig. 3

Bit-pattern-printing results. (a) Full-view SEM image of the printed pattern. The pattern shows two lines of text and is pixelated. Top line: Chinese words, printed by channel 1 with PPI; bottom line: English words (translation of the text in the top line), printed by channel 2 without PPI. Scale bar: 2  μm. (b), (c) Enlarged views of the yellow and blue boxes in (a), respectively; the horizontal and vertical pitches of the bits are 200 nm. Scale bars: 1  μm.

AP_4_6_066002_f003.png

3.3.

Three-Dimensional Structure Printing

To test the parallel printing of an actual 3D nanostructure, a metamaterial architecture50 (a cube) was printed. This cube was used as a bench sample in Ref. 42. Here we considered two cells as bench samples: one containing 2×2×2 units and the other containing 3×3×3 units. The unit 3D models and more relative results are shown in Fig. S12 in the Supplementary Material. Because of the individual control of the light beam, the distance between the two focal spots did not need to match the size of the unit to make one spot print one unit, which makes the system more flexible. In fact, we could also have generated more spots in the focal plane to print the units simultaneously using the SLM, but that was out of the scope of this experiment. For this micron-scale structure, a sub-100-nm feature size was not required; therefore, the cells were printed without PPI. The distance between the two spots was adjusted to 50  μm, and the power of a single spot was 31.5 mW. The objective lens was changed to 40× (Olympus, NA 1.40, Tokyo, Japan), and the focal-spot speed was 50  mm/s [step size: 100  nm(x)×100  nm(y)×200  nm(z)]. The corresponding results are presented in Fig. 4, where the size of each cell is 200  μm. Three-fold stitching was required, and the areas printed by different spots are marked by different colors in Figs. 4(b) and 4(e).

Fig. 4

Metamaterial cubic-unit printing results: (a) SEM image of a 2×2×2 unit cell, (b) top view of (a), (c) zoomed-in view of the yellow box in (a), (d) SEM image of a 3×3×3 unit cell, (e) top view of (d), and (f) zoomed-in view of the yellow box in (d). In (b) and (e), the portions corresponding to the light-blue stripes were printed by channel 1, and those indicated by the dark-red stripes were printed by channel 2. Scale bars: 50  μm.

AP_4_6_066002_f004.png

To demonstrate the feasibility of the 3D fabrication method further, additional 3D structures were printed. First, two cubic frames were printed by the two spots simultaneously. The two frames were of the same size but had different patterns (squares and circles), as shown in Fig. 5(a). Each spot printed one frame, the separation of the two spots was 20  μm, and the side length was 18  μm. Second, three types of continuous 3D nanostructures were printed: periodic, wire, and spherical structures, and oblique-view SEM images of these structures are provided in Figs. 5(b)5(d), respectively. Figure 5(b) shows a periodic fence array with 10 hexagonal cells; each cell has a side length of 8  μm and a height of 10  μm. The photonic wire is a functional nanostructure used to connect integrated circuits across chip boundaries. We printed a photonic-wire structure model containing four wires crossing each other spatially [Fig. 5(c)]. A 32-μm-diameter buckyball model was also printed [Fig. 5(d)]. For these structures, the objective lens was changed back to 100×. The focal-spot power was 15.2 mW, and the speed was set to 30  mm/s [step size: 100  nm(x)×100  nm(y)×200  nm(z)]. A few 2.5D structures were also printed as additional evidence, and the results can be found in Fig. S13 in the Supplementary Material.

Fig. 5

Oblique-view SEM images of 3D nanostructures parallel-printed using two spots. (a) Two cubical box frames, (b) periodic structure: hexagonal fence, (c) wire structure: nanophotonic wires, and (d) spherical structure: buckyball model. Scale bars: 10  μm.

AP_4_6_066002_f005.png

4.

Discussion and Outlook

Multifocus parallel scanning and the PPI technique can enable potential breakthroughs in DLW optical fabrication. Herein, we proposed a two-focus parallel scanning strategy with minimal hardware updates for system stability. Furthermore, the identical on–off control of each focus verifies the possibility of rapid parallel lithography of nonperiodic patterns and structures, increasing the flexibility of DLW. The proposed method enables rapid and identical on–off control of each focus with a modulation frequency on the order of a megahertz, which can also be achieved using an SLM. However, the SLM frequency is the maximum possible on–off frequency, and the typical frame rate of the SLM is only 60 Hz (the highest is 1 kHz, which is still considerably lower than the AOM frequency). If the pattern to be printed is significantly complex and nonperiodic, resulting in a beam on–off frequency on the order of a megahertz, a system that uses an SLM to generate multiple foci is unsuitable. One solution to this problem is to decrease the scanning speed to lower the on–off frequency. Notably, it is difficult to realize parallel printing of complex and nonperiodic patterns by employing an SLM alone without compromising the scanning speed. Our method addresses this problem using an AOM to modulate every subbeam. It can, therefore, enable the parallel printing of nonperiodic and complex patterns without compromising the scanning speed. Moreover, because our system uses SLMs, it can still generate multiple foci to print identical patterns or use a relatively low on–off beam frequency to print nonidentical ones.

For a DLW system, reducing the time cost required to fabricate large-scale structures or patterns is a major challenge. Parallel scanning is a feasible solution to this problem. However, another important issue is related to the stitching process, particularly for systems using galvanometer scanners. In the proposed system, the separation distance between the two spots can be controlled by adjusting the tilt parameter following the Zernike polynomials. However, it is impossible to increase the distance without any limits. Therefore, when printing certain large structures or patterns, a stitching process is required, which introduces artifact-related issues. The mechanism that causes artifacts in the stitching process is complicated. The factors affecting this mechanism include the properties of the photoresist; mechanical properties of the structure to be printed; printing parameters; and uniformity in the shape, power, and focus depth of the two spots. In galvanometer-based multifocal-spot systems, stitching-induced artifacts constitute a considerable problem that should be addressed in the future research.

The proposed system can provide a sub-50-nm feature size in direct-writing lithography and extend the potential application range of DLW optical fabrication. In particular, for the fabrication of certain 3D structures with dimensions of several hundred nanometers, traditional 2PP-DLW with a feature size of more than 100 nm may encounter sampling and subdivision issues owing to the relatively large pixel volumes, which may lead to increased roughness of the fabricated structures. Electron beam lithography provides smaller feature sizes; however, its ability to fabricate special 3D structures is quite limited. By using PPI, the proposed system enables the DLW optical fabrication of various fine 3D structures, such as those of nanoscale optical elements including blazed gratings, microlens arrays, microfluidic structures, and metasurfaces. Therefore, the proposed system can serve as a useful tool for supporting the development of numerous fields.

5.

Conclusion

Our proposed P3L system improves the throughput of DLW by fully utilizing the polarized components of the light. The printing efficiency achieved with a double-beam path is twice that of traditional DLW. Moreover, the two channels in the P3L system can execute different printing tasks, enabling it to fabricate not only periodic structures but also highly complex ones. Further, a sub-40-nm 2D feature size and a sub-20-nm suspended line width were achieved using the PPI mechanism. The parallel PPI-DLW method can improve the throughput of optical nanofabrication. However, despite the improved efficiency, a large performance gap remains between this approach and projection lithography. Additional multifocal-system strategies should be explored in future work, especially ones involving rapid independent control of focal spots.

Acknowledgments

We would like to thank Dr. Xiaoming Shen of the Research Center for Intelligent Chips and Devices, Zhejiang Lab, for the assistance with the SEM and suggestions regarding bit-dot-pattern printing. This research was financially supported by the National Key Research and Development Program of China (Grant No. 2021YFF0502700), the National Natural Science Foundation of China (Grant Nos. 62105298, 52105565, and 22105180), China Postdoctoral Science Foundation (Grant Nos. 2020M671823 and 2020M681956), the Natural Science Foundation of Zhejiang Province, China (Grant Nos. LD21F050002, LQ22F050017, and LQ22F050015), and the Major Scientific Project of Zhejiang Lab, China (Grant No. 2020MC0AE01). The authors have no competing interests to declare.

Code, Data, and Material Availability

Data underlying the results presented in this paper may be obtained from the corresponding authors upon reasonable request. All software is also available from the corresponding authors upon reasonable request.

References

1. 

R. Wollhofen et al., “120 nm resolution and 55 nm structure size in STED-lithography,” Opt. Express, 21 (9), 10831 –10840 https://doi.org/10.1364/OE.21.010831 OPEXFF 1094-4087 (2013). Google Scholar

2. 

T. A. Klar, R. Wollhofen and J. Jacak, “Sub-Abbe resolution: from STED microscopy to STED lithography,” Phys. Scr., T162 014049 https://doi.org/10.1088/0031-8949/2014/T162/014049 PHSTBO 0031-8949 (2014). Google Scholar

3. 

S. W. Hell, “Microscopy and its focal switch,” Nat. Methods, 6 24 –32 https://doi.org/10.1038/nmeth.1291 1548-7091 (2009). Google Scholar

4. 

M. Elmeranta et al., “Characterization of nanostructures fabricated with two-beam DLW lithography using STED microscopy,” Opt. Mater. Express, 6 (10), 3169 –3179 https://doi.org/10.1364/OME.6.003169 (2016). Google Scholar

5. 

S. W. Hell and J. Wichmann, “Breaking the diffraction resolution limit by stimulated emission: stimulated-emission-depletion fluorescence microscopy,” Opt. Lett., 19 (11), 780 –782 https://doi.org/10.1364/OL.19.000780 OPLEDP 0146-9592 (1994). Google Scholar

6. 

T. A. Klar et al., “Fluorescence microscopy with diffraction resolution barrier broken by stimulated emission,” Proc. Natl. Acad. Sci. U. S. A., 97 (15), 8206 –8210 https://doi.org/10.1073/pnas.97.15.8206 (2000). Google Scholar

7. 

K. I. Willig et al., “STED microscopy reveals that synaptotagmin remains clustered after synaptic vesicle exocytosis,” Nature, 440 (7086), 935 –939 https://doi.org/10.1038/nature04592 (2006). Google Scholar

8. 

Z. Gan et al., “Three-dimensional deep sub-diffraction optical beam lithography with 9 nm feature size,” Nat. Commun., 4 2061 https://doi.org/10.1038/ncomms3061 NCAOBW 2041-1723 (2013). Google Scholar

9. 

J. Fischer et al., “Exploring the mechanisms in STED-enhanced direct laser writing,” Adv. Opt. Mater., 3 (2), 221 –232 https://doi.org/10.1002/adom.201400413 2195-1071 (2015). Google Scholar

10. 

T. F. Scott et al., “Two-color single-photon photoinitiation and photoinhibition for subdiffraction photolithography,” Science, 324 (5929), 913 –917 https://doi.org/10.1126/science.1167610 SCIEAS 0036-8075 (2009). Google Scholar

11. 

J. Fischer, G. von Freymann and M. Wegener, “The materials challenge in diffraction-unlimited direct-laser-writing optical lithography,” Adv. Mater., 22 (32), 3578 –3582 https://doi.org/10.1002/adma.201000892 ADVMEW 0935-9648 (2010). Google Scholar

12. 

J. T. Fourkas, “Nanoscale photolithography with visible light,” J. Phys. Chem. Lett., 1 (8), 1221 –1227 https://doi.org/10.1021/jz1002082 JPCLCD 1948-7185 (2010). Google Scholar

13. 

J. Fischer and M. Wegener, “Ultrafast polymerization inhibition by stimulated emission depletion for three-dimensional nanolithography,” Adv. Mater., 24 (10), OP65 –OP69 https://doi.org/10.1002/adma.201103758 ADVMEW 0935-9648 (2012). Google Scholar

14. 

R. Wollhofen et al., “Functional photoresists for sub-diffraction stimulated emission depletion lithography,” Opt. Mater. Express, 7 (7), 2538 –2559 https://doi.org/10.1364/OME.7.002538 (2017). Google Scholar

15. 

Y. Cao et al., “High-photosensitive resin for super-resolution direct-laser-writing based on photoinhibited polymerization,” Opt. Express, 19 (20), 19486 –19494 https://doi.org/10.1364/OE.19.019486 OPEXFF 1094-4087 (2011). Google Scholar

16. 

X. He et al., “STED direct laser writing of 45 nm width nanowire,” Micromachines, 10 (11), 726 https://doi.org/10.3390/mi10110726 (2019). Google Scholar

17. 

J. Fischer and M. Wegener, “Three-dimensional optical laser lithography beyond the diffraction limit,” Laser Photonics Rev., 7 (1), 22 –44 https://doi.org/10.1002/lpor.201100046 (2013). Google Scholar

18. 

K. Sugioka et al., “Femtosecond laser 3D micromachining: a powerful tool for the fabrication of microfluidic, optofluidic, and electrofluidic devices based on glass,” Lab Chip, 14 (18), 3447 –3458 https://doi.org/10.1039/C4LC00548A LCAHAM 1473-0197 (2014). Google Scholar

19. 

K. Sugioka and Y. Cheng, “Femtosecond laser three-dimensional micro- and nanofabrication,” Appl. Phys. Rev., 1 (4), 041303 https://doi.org/10.1063/1.4904320 (2014). Google Scholar

20. 

L. Q. Tao et al., “A flexible 360-degree thermal sound source based on laser induced graphene,” Nanomaterials, 6 (6), 112 https://doi.org/10.3390/nano6060112 (2016). Google Scholar

21. 

C. Kachris and I. Tomkos, “A survey on optical interconnects for data centers,” IEEE Commun. Surv. Tutorials, 14 (4), 1021 –1036 https://doi.org/10.1109/SURV.2011.122111.00069 (2012). Google Scholar

22. 

R. R. Gattass and E. Mazur, “Femtosecond laser micromachining in transparent materials,” Nat. Photonics, 2 (4), 219 –225 https://doi.org/10.1038/nphoton.2008.47 NPAHBY 1749-4885 (2008). Google Scholar

23. 

H. Zeng et al., “High-resolution 3D direct laser writing for liquid-crystalline elastomer microstructures,” Adv. Mater., 26 (15), 2319 –2322 https://doi.org/10.1002/adma.201305008 ADVMEW 0935-9648 (2014). Google Scholar

24. 

B. Buchegger et al., “Stimulated emission depletion lithography with mercapto-functional polymers,” ACS Nano, 10 (2), 1954 –1959 https://doi.org/10.1021/acsnano.5b05863 ANCAC3 1936-0851 (2016). Google Scholar

25. 

M. Deubel et al., “Direct laser writing of three-dimensional photonic-crystal templates for telecommunications,” Nat. Mater., 3 (7), 444 –447 https://doi.org/10.1038/nmat1155 NMAACR 1476-1122 (2004). Google Scholar

26. 

W. Gao et al., “Direct laser writing of micro-supercapacitors on hydrated graphite oxide films,” Nat. Nanotechnol., 6 (8), 496 –500 https://doi.org/10.1038/nnano.2011.110 NNAABX 1748-3387 (2011). Google Scholar

27. 

Z.-L. Wu et al., “Polymer-based device fabrication and applications using direct laser writing technology,” Polymers, 11 (3), 553 https://doi.org/10.3390/polym11030553 (2019). Google Scholar

28. 

P. Mueller et al., “Molecular switch for sub-diffraction laser lithography by photoenol intermediate-state cis–trans isomerization,” ACS Nano, 11 (6), 6396 –6403 https://doi.org/10.1021/acsnano.7b02820 ANCAC3 1936-0851 (2017). Google Scholar

29. 

M. Wiesbauer et al., “Nano-anchors with single protein capacity produced with STED lithography,” Nano Lett., 13 (11), 5672 –5678 https://doi.org/10.1021/nl4033523 NALEFD 1530-6984 (2013). Google Scholar

30. 

C. Wolfesberger et al., “Streptavidin functionalized polymer nanodots fabricated by visible light lithography,” J. Nanobiotechnol., 13 (1), 27 https://doi.org/10.1186/s12951-015-0084-6 (2015). Google Scholar

31. 

S. K. Saha et al., “Scalable submicrometer additive manufacturing,” Science, 366 (6461), 105 –109 https://doi.org/10.1126/science.aax8760 SCIEAS 0036-8075 (2019). Google Scholar

32. 

K. Kataoka et al., “Laser printer optics with use of slant scanning of multiple beams,” Appl. Opt., 36 (25), 6294 –6307 https://doi.org/10.1364/AO.36.006294 APOPAI 0003-6935 (1997). Google Scholar

33. 

X. Li et al., “Multifocal optical nanoscopy for big data recording at 30 TB capacity and gigabits/second data rate,” Optica, 2 (6), 567 –570 https://doi.org/10.1364/OPTICA.2.000567 (2015). Google Scholar

34. 

J. Jin et al., “Multi-channel vortex beam generation by simultaneous amplitude and phase modulation with two-dimensional metamaterial,” Adv. Mater. Technol., 2 (2), 1600201 https://doi.org/10.1002/admt.201600201 (2017). Google Scholar

35. 

F. Formanek et al., “Three-dimensional fabrication of metallic nanostructures over large areas by two-photon polymerization,” Opt. Express, 14 (2), 800 –809 https://doi.org/10.1364/OPEX.14.000800 OPEXFF 1094-4087 (2006). Google Scholar

36. 

J. I. Kato et al., “Multiple-spot parallel processing for laser micronanofabrication,” Appl. Phys. Lett., 86 (4), 044102 https://doi.org/10.1063/1.1855404 APPLAB 0003-6951 (2005). Google Scholar

37. 

X. Z. Dong, Z. S. Zhao and X. M. Duan, “Micronanofabrication of assembled three-dimensional microstructures by designable multiple beams multiphoton processing,” Appl. Phys. Lett., 91 (12), 124103 https://doi.org/10.1063/1.2789661 APPLAB 0003-6951 (2007). Google Scholar

38. 

S. D. Gittard et al., “Fabrication of microscale medical devices by two-photon polymerization with multiple foci via a spatial light modulator,” Biomed. Opt. Express, 2 (11), 3167 –3178 https://doi.org/10.1364/BOE.2.003167 BOEICL 2156-7085 (2011). Google Scholar

39. 

W. Yan, B. P. Cumming and M. Gu, “High-throughput fabrication of micrometer-sized compound parabolic mirror arrays by using parallel laser direct-write processing,” J. Opt., 17 (7), 075803 https://doi.org/10.1088/2040-8978/17/7/075803 (2015). Google Scholar

40. 

L. Yang et al., “Parallel direct laser writing of micro-optical and photonic structures using spatial light modulator,” Opt. Lasers Eng., 70 26 –32 https://doi.org/10.1016/j.optlaseng.2015.02.006 (2015). Google Scholar

41. 

Q. Geng et al., “Ultrafast multi-focus 3-D nano-fabrication based on two-photon polymerization,” Nat. Commun., 10 2179 https://doi.org/10.1038/s41467-019-10249-2 NCAOBW 2041-1723 (2019). Google Scholar

42. 

V. Hahn et al., “Rapid assembly of small materials building blocks (voxels) into large functional 3D metamaterials,” Adv. Funct. Mater., 30 (26), 1907795 https://doi.org/10.1002/adfm.201907795 AFMDC6 1616-301X (2020). Google Scholar

43. 

J. Miao, D. Sayre and H. N. Chapman, “Phase retrieval from the magnitude of the Fourier transforms of nonperiodic objects,” J. Opt. Soc. Am. A, 15 (6), 1662 –1669 https://doi.org/10.1364/JOSAA.15.001662 JOAOD6 0740-3232 (1998). Google Scholar

44. 

S. G. Podorov, K. M. Pavlov and D. M. Paganin, “A non-iterative reconstruction method for direct and unambiguous coherent diffractive imaging,” Opt. Express, 15 (16), 9954 –9962 https://doi.org/10.1364/OE.15.009954 OPEXFF 1094-4087 (2007). Google Scholar

45. 

M. O. Lenz et al., “3-D stimulated emission depletion microscopy with programmable aberration correction,” J. Biophotonics, 7 (1–2), 29 –36 https://doi.org/10.1002/jbio.201300041 (2014). Google Scholar

46. 

D. Zhu et al., “Compact three-dimensional super-resolution system based on fluorescence emission difference microscopy,” Opt. Commun., 405 157 –163 https://doi.org/10.1016/j.optcom.2017.08.017 OPCOB8 0030-4018 (2017). Google Scholar

47. 

T. J. Gould et al., “Adaptive optics enables 3D STED microscopy in aberrating specimens,” Opt. Express, 20 (19), 20998 –21009 https://doi.org/10.1364/OE.20.020998 OPEXFF 1094-4087 (2012). Google Scholar

48. 

S. Deng et al., “Investigation of the influence of the aberration induced by a plane interface on STED microscopy,” Opt. Express, 17 (3), 1714 –1725 https://doi.org/10.1364/OE.17.001714 OPEXFF 1094-4087 (2009). Google Scholar

49. 

C. Cao et al., “Dip-in photoresist for photoinhibited two-photon lithography to realize high-precision direct laser writing on wafer,” ACS Appl. Mater. Interfaces, 14 (27), 31332 –31342 https://doi.org/10.1021/acsami.2c08063 AAMICK 1944-8244 (2022). Google Scholar

50. 

T. Frenzel, M. Kadic and M. Wegener, “Three-dimensional mechanical metamaterials with a twist,” Science, 358 (6366), 1072 –1074 https://doi.org/10.1126/science.aao4640 SCIEAS 0036-8075 (2017). Google Scholar

Biographies of the authors are not available.

CC BY: © The Authors. Published by SPIE and CLP under a Creative Commons Attribution 4.0 International License. Distribution or reproduction of this work in whole or in part requires full attribution of the original publication, including its DOI.
Dazhao Zhu, Liang Xu, Chenliang Ding, Zhenyao Yang, Yiwei Qiu, Chun Cao, Hongyang He, Jiawei Chen, Mengbo Tang, Lanxin Zhan, Xiaoyi Zhang, Qiuyuan Sun, Chengpeng Ma, Zhen Wei, Wenjie Liu, Xiang Fu, Cuifang Kuang, Haifeng Li, and Xu Liu "Direct laser writing breaking diffraction barrier based on two-focus parallel peripheral-photoinhibition lithography," Advanced Photonics 4(6), 066002 (23 November 2022). https://doi.org/10.1117/1.AP.4.6.066002
Received: 21 August 2022; Accepted: 1 November 2022; Published: 23 November 2022
Lens.org Logo
CITATIONS
Cited by 13 scholarly publications.
Advertisement
Advertisement
KEYWORDS
Printing

Spatial light modulators

Lithography

Multiphoton lithography

Diffraction

Scanning electron microscopy

Photonics

Back to Top