This article shows a dual-frequency OPO with multi-grating (28.5-31.5 μm) periodically poled MgO:LiNbO3 (MgO:PPLN) pumped by a dual-frequency continuous wave at 1.064 μm. The wavelengths of idler and signal varying versus temperature at different periods of inverted domains were numerical simulated. It proves that as the temperature rises, or as the poling period increases, the idler wavelength shortens and signal wavelength lengthens. The pump is a 30 W dual-frequency fiber laser MOPA with beat note frequency varying from 125 MHz to 175 MHz. The pump threshold of the bow-tie ring cavity OPO was 3 W. An average dual-frequency idler output power of 2.6 W was obtained when the pump power was 17.2 W at 45 °C. The idler wavelength was 3.4 μm when the poling period was 30.5 μm. The idler wavelength could be tuned from 2.9 μm to 3.9 μm by changing the temperature and the poling period, and the beat note frequency was proved to be equal to that of the pump.
This article shows a dual-frequency OPO with multi-grating (28.5-31.5 μm) periodically poled MgO:LiNbO3 (MgO:PPLN) pumped by a dual-frequency continuous wave at 1.064 μm. The wavelengths of idler and signal varying versus temperature at different periods of inverted domains were numerical simulated. It proves that as the temperature rises, or as the poling period increases, the idler wavelength shortens and signal wavelength lengthens. The pump is a 30 W dual-frequency fiber laser MOPA with beat note frequency varying from 125 MHz to 175 MHz. The pump threshold of the bow-tie ring cavity OPO was 3 W. An average dual-frequency idler output power of 2.6 W was obtained when the pump power was 17.2 W at 45 °C. The idler wavelength was 3.4 μm when the poling period was 30.5 μm. The idler wavelength could be tuned from 2.9 μm to 3.9 μm by changing the temperature and the poling period, and the beat note frequency was proved to be equal to that of the pump.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.